Optical fiber drawing furnace having adjustable partitions

ABSTRACT

A furnace for drawing an optical fiber provided with a muffle tube ( 10 ) and inner tubes ( 5,5 ′) connected to the upper end of the core tube, wherein a preform ( 1 ) supported by a dummy rod ( 2 ) at the upper part thereof is disposed inside the muffle tube ( 10 ) and inner tubes ( 5,5 ′) so as to be movable downward together with dummy rod ( 2 ), the preform ( 1 ) is heated and melted by a heater ( 11 ) from the outside of the muffle tube ( 10 ) and an optical fiber ( 1   a ) is pulled out from the lower end of the preform ( 1 ); the furnace is further provided with one or a plurality of sets of separating plates ( 4, 17 ) adapted to partition a space in the inner tubes ( 5, 5 ′) above the preform ( 1 ) into a plurality of portions in the advance direction of the preform and disposed in the space, and with gas blowing inlets ( 8 ) disposed in the parts of wall surfaces of the inner tubes ( 5, 5 ′) which are below the separating plates ( 4,17 ) and adapted to blow an inert gas into the inner tubes ( 5,5 ′) and the muffle tube ( 10 ), thereby preventing variations in diameter of the optical fiber ( 1   a ).

TECHNICAL FIELD

The present invention relates to a furnace and a method for drawing anoptical fiber from heated and molten preform.

BACKGROUND ART

Various techniques have been known relating to a furnace for drawing anoptical fiber from heated preform formed with silica glass as a maincomponent, and they are described in Japanese Patent No. 2,542,679,Japanese Patent Laid-Open No. 147969/1993 and Japanese Patent Laid-OpenNo. 2832/1997. Since the figures and terminology in these prior artsdiffer partially from those used in this invention, descriptions will bemade below where they are interpreted according to the figures andterminology used in this invention in order to clarify the differencebetween the prior arts and this invention.

A main part of the furnace for drawing an optical fiber disclosed inJapanese Patent No. 2,542,679 is shown in FIG. 8, in which numeral 21denotes a preform, 21 a denotes an optical fiber, 22 denotes an innertube, 22 a denotes a gas blowing inlet, 23 denotes an outer tube, 24denotes a gas supplying inlet, 24 a denotes a gas passage, 25 denotes adummy rod, 25 a denotes a connecting part, 26 denotes a retainer, 27denotes a seal piston, 28 denotes a muffle tube, and 29 denotes aheater.

In the furnace for drawing an optical fiber, the dummy rod 25 and thepreform 21 are arranged inside the muffle tube 28 and the inner tube 22arranged to be connected to an upper end of the muffle tube 28, whilethey are connected via the connecting part 25 a and are descendedtogether. The vicinity of a lower end of the preform 21 is meltedthrough heating by the heater 29 arranged outside the muffle tube 28,and the optical fiber 21 a is drawn downward from the lower end of thepreform 21. The inner tube 22 arranged to be connected to the upper endof the muffle tube 28 is to contain the long preform 21 on starting thedrawing.

The gas passage 24 a is formed between the inner tube 22 and the outertube 23 arranged outside the same, and an inert gas is supplied from thegas supplying inlet 24 to the gas passage 24 a, so as to blow the inertgas into the inside of the inner tube 22 from the numerous gas blowinginlets 22 a provided circumferentially and in the height direction onthe wall surface of the inner tube 22. The inert gas is flowed insidethe inner tube 22 and the muffle tube 28 to prevent oxidationdeterioration of the muffle tube and the like, and when the temperaturedistribution of the inert gas by heating and the flow of the inert asare not uniform, fluctuation of the diameter of the optical fiber drawnfrom the preform is liable to occur.

Therefore, in this example of the furnace for drawing an optical fiber,the seal piston 27 connected to the dummy rod 25 via the retainer 26 andmoved with the dummy rod 25 is provided at the dummy rod 25 arranged onthe upper part of the preform 21. In the beginning of drawing, the dummyrod 25 and the seal piston 27 are in the upper part because the preformis long. With proceeding the drawing, the preform 21 is shortened fromthe lower end, and is descended, and thus, the dummy rod 25 and the sealpiston 27 are also descended.

In this case, if the seal piston 27 were not present, the space betweenthe dummy rod 25 and the inner tube 22 would gradually increase, butbecause the seal piston 27 is present, the volume of space above thepreform 21 is substantially constant. Therefore, it has been said thatturbulence of the stream of the inert gas in the space between thepreform 21 and the seal piston 27 occurs only scarcely due to theprovision of the seal piston 27.

In the furnace using the seal piston for drawing an optical fiber, whenthe preform has a length of 1.5 m or more, the seal piston necessarilyhas an proportionate length, and the weight thereof becomes also heavy.Because a supporting member for supporting them at the upper part mustwithstand the weight of the preform and the seal piston, the supportingmember becomes also necessarily large. Because the seal piston mustresist to high temperature, a heat resistant material, such as carbon,quartz and the like, is necessarily used for the seal piston, and itbecomes costly when it is of large scale.

Furthermore, because the seal piston moves as sliding on the inner wallsurface of the inner tube, dust is liable to come from the sliding part,which may adversely affect the strength of the drawn optical fiber.

Furthermore, as the seal piston descents, the numerous gas blowinginlets provided in the wall surface of the inner tube are sealed one byone from the upper part with the seal piston, a precise controller forcontinuously controlling the gas flow rate is necessary to maintain theconstant flow rate of the stream of the inert gas.

A furnace for drawing an optical fiber disclosed in Japanese PatentLaid-Open No. 147969/1993 will then be described. A main part of thefurnace for drawing an optical fiber is shown in FIG. 9. In FIG. 9, thesame references as in FIG. 8 show the same components. Numeral 30denotes a separating plate, 30 a denotes a gap, 30 b denotes pores, 31 adenotes an upper space, 31 b denotes a lower space, and 32 denotes anupper lid. The furnace for drawing an optical fiber shown in FIG. 9 isdifferent from that shown in FIG. 8 in the following points. There is nomember corresponding to the seal piston in FIG. 8, and an upper end ofan inner tube 22 is closed with the upper lid 32 except for the partthrough which a dummy rod 25 penetrates.

In the furnace for drawing an optical fiber, a preform 21 is arrangedinside a muffle tube 28 and the inner tube 22 connected to an upper endthereof, and the preform 21 is supported by hanging by the dummy rod 25through a connecting part 25 a. The vicinity of the lower end of thepreform 21 is heated and melted by a heater 29 arranged outside themuffle tube 28, and an optical fiber 21 a is drawn downward.

An outer tube 23 is arranged concentrically outside the inner tube 22,and an inert gas is blown into the inside of the inner tube via a gasblowing inlet 22 a through a gas passage 24 a formed with the outer tube23 and the inner tube 22. The inert gas is introduced to the gas passage24 a from a gas supplying inlet 24. The inert gas blown into the innertube 22 descends through the space between (the inner tube 22 and themuffle tube 28) and (the preform 21 or the dummy rod 25), then it isexhausted through the vicinity of the optical fiber 21 a.

The space inside the inner tube 22 is separated by the separating plate30 comprising a quartz plate or the like into an upper part and a lowerpart, and the inert gas flows from the upper space 31 a of theseparating plate 30 to the lower space 31 b through the gap 30 a betweenthe separating plate 30 and the inner tube 22 or the pores 30 b providedin the separating plate 30. Because the lower space 31 b is of arelatively high temperature and turbulence of the gas stream isdecreased owing to the presence of the separating plate 30, it has beensaid that an optical fiber having a small fluctuation in diameter can bedrawn even in the case of a large preform.

However, in the case of this furnace for drawing an optical fiber, whenthe preform 21 becomes small with proceeding the drawing, the upperspace 31 a becomes large. On the other hand, the temperature near theupper end of the preform 21 is increased by heating the vicinity of thelower end of the preform 21, and said temperature becomes higher whenthe preform becomes small. Because of the presence of the separatingplate 30 comprising a quartz plate, the temperature is somewhatdecreased above the, separating plate, but it becomes 550° C. or morenear the lower end of the upper space 31 a. At this time, thetemperature near the upper end of the upper space 31 a is about 200° C.to form a considerable difference in temperature between the upper partand the lower part inside the upper space 31 a, therefore convection isliable to be caused. The convection causes fluctuation in volume of theinert gas, and the fluctuation is transmitted to the lower space 31 b bythe flow of the inert gas through the gap 30 a or the pore 30 b of theseparating plate 30. Thus, fluctuation in flow of the inert gas near theoptical fiber occurs. As a result, the amount of heat transmission ischanged by the fluctuation of the inert gas to easily cause fluctuationin viscosity and softened amount of glass, and thus it is difficult tosuppress fluctuation in fiber diameter to a small value less than theprescribed value.

A furnace for drawing an optical fiber disclosed in Japanese PatentLaid-Open No. 2832/1997 will then be described. The furnace for drawingan optical fiber is shown in FIG. 10. In FIG. 10, the correspondingreferences as in FIG. 8 show the same components. Numeral 33 denotes anupper space above the preform, and 34 denotes an auxiliary heater. Inthe furnace for drawing an optical fiber, a preform 21 is arrangedinside a muffle tube 28 and the inner tube 22 connected to an upper endthereof, being supported by hanging by the dummy rod 25, and thevicinity of a lower end of the preform 21 is heated and melted by aheater 29 arranged outside the muffle tube 28, so as to draw an opticalfiber 21 a downward.

An outer tube 23 is arranged outside the inner tube 22 concentrically,and an inert gas is blown into the inside of the inner tube via a gasblowing inlet 22 a through a gas passage 24 a formed with the outer tube23 and the inner tube 22. Because the vicinity of the upper end of thepreform 21 becomes a high temperature of 1,000° C. or more by heatingthe vicinity of the lower end of the preform 21, a large temperaturedifference formed between the upper part and the lower part of the space33 above the preform.

In order to decrease the temperature difference, the auxiliary heater 34is arranged outside the upper end of the inner tube 22 to heat thevicinity of the upper end of the inner tube 22. Thus, the verticaltemperature difference of the space 33 between the inner tube 22 and thedummy rod 25 above the preform is decreased by the heating by theauxiliary heater 34 to prevent the convection from occurring at thespace 33, and fluctuation in diameter of the optical fiber 21 a drawnfrom the preform 21 is decreased.

However, in the case of this furnace for drawing an optical fiber,because the space 33 above the preform becomes large as the drawing of alarge scale preform proceeds, it is difficult to make the temperatureuniform inside the space solely by an auxiliary heater 34 arrangedoutside the upper part of the inner tube 22.

It is then considered that several auxiliary heaters are arrangedvertically not only at the upper part but also at the lower part of theinner tube, and by controlling the temperature of each auxiliary heater,the temperature of the space above the preform is made uniform. However,there are problems that cost of the apparatus becomes increased, and thetemperature control becomes complicated.

Disclosure of Invention

The invention is to provide a furnace for drawing an optical fiber and amethod for drawing an optical fiber to solve the problems associatedwith the conventional art described in the foregoing.

The furnace for drawing an optical fiber according to the inventioncomprises a muffle tube and an inner tube connected to an end of themuffle tube. The preform is arranged inside the muffle tube and theinner tube and supported by a dummy rod at an upper part thereof in sucha manner that the preform descends with the dummy rod. The preform isheated from outside of the muffle tube by a heater, and melted so as todraw an optical fiber from a lower end of the preform. One set or pluralsets of separating plates separating a space inside the inner tube abovethe preform into plural parts in an advancing direction of the preformare arranged inside the space, and a gas blowing inlet for blowing aninert gas into the inner tube and the muffle tube is provided at thewall of the inner tube at a part under the separating plates.

Therefore, the inert gas entered from the gas blowing inlet mainly flowsdownward, and thus the gas in the upper space of the separating plateabove the preform less influences the conditions of the drawing of thepreform. Accordingly, the drawing is stably continued, and fluctuationin fiber diameter is decreased. Therefore, an optical fiber produced byusing this furnace for drawing an optical fiber has a substantiallyconstant outer diameter in the longitudinal direction, and has smallfluctuation in transmission characteristics. Owing to the use of asimple separating plate but not using a large member such as a sealpiston, the cost of the apparatus is low, and since heavy sliding as inthe seal piston does not occur, dust formed by sliding is so minimalthat it doesn't adversely affect the strength of the optical fiber.

While the separating plates comprise plural sets of separating platesarranged as being penetrated by the dummy rod, and the plural sets ofseparating plates descend with the descent of the dummy rod, therespective sets of the plural sets of separating plates are stopped onthe inner wall surface of the inner tube one by one, so that the spaceinside the inner tube above the preform is respectively separated intoan upper part and a lower part by the stopped separating plates. Thus,because the space inside the inner tube can be separated by pluralpositions into suitable sizes, the flow of the inert gas inside theinner tube can be further stabilized even when the preform becomes smalland the space inside the inner tube is enlarged with proceeding thedrawing of the optical fiber.

While the respective sets of separating plates may each comprise onedisk-shaped plate, the sets of separating plates may each be constitutedby two plate members of an outer member and an inner member. In thiscase, the outer member has an outer diameter that is the same as theinner diameter of the inner tube at a position where the separatingplate is stopped, and has a center hole diameter that is larger than theouter diameter of dummy rod so as to absorb the deviation from theconcentric condition of the inner tube and the dummy rod. The innermember has an outer diameter that is larger than the center holediameter of the outer member and smaller than the outer diameter of theouter member, and has a center hole diameter larger than an outerdiameter of the dummy rod by 2 to 10 mm.

When the dummy rod penetrates both the members with the inner memberbeing placed at upper side and the outer member being placed at lowerside, the upward inner member is supported by being placed on the outermember. By constituting each of the sets of separating plates of anouter member and an inner member, even when the concentric condition ofthe inner tube and the dummy rod is deviated by rolling of the preformto cause decentering, the upper member moves in the radial direction bysliding on the lower member, and no such phenomenon that the inner wallsurface of the inner tube is damaged by the separating plate occurs.

Alternatively, one or plural sets of separating plates may be arrangednear the lower end of the dummy rod or at the upper part of the preformby fixing to the dummy rod, the connecting part or the preform, and theydescend with the descent of the preform without stopping on the way onthe inner wall of the inner tube. Accordingly, the space between theseparating plates and the preform can be unchanged and constant evenwhen the preform is shortened, and thus the flow of the gas in the spaceabove the preform can be stabilized. It is also possible in this casethat the respective sets of separating plates are each constituted by anouter member and an inner member. In this case, however, the outerdiameter of the outer member must be smaller than the inner diameter ofthe inner tube by 5 to 10 mm, and the center hole diameter of the outermember must be larger than the outer diameter of the dummy rod. Theouter diameter of the inner member must be larger than the center holediameter of the outer member but smaller than the outer diameter of theouter member. The center hole diameter of the inner member must be thesame as or larger than the outer diameter of the dummy rod. The innermember is then supported by the dummy rod or the connecting part withthe inner member being downward and the outer member being upward.

By constituting each of the respective sets of separating plates by theouter member and the inner member, even in the case where the concentriccondition is deviated by rolling of the preform to cause decentering,the upper member moves in the radial direction by sliding on the lowermember, and no such phenomenon that the inner wall surface of the innertube is damaged by the separating plate occurs.

When plural protrusions are provided on an outer periphery of theseparating plate, the sliding friction coefficient of the separatingplate to the inner wall surface of the inner tube on descending can bereduced, so as not to damage the inner tube, because only theprotrusions are in contact with the inner wall surface of the innertube.

By forming the separating plate with a heat insulating material, heattransferred from the upper end of the heated preform to the upper spaceabove the separating plate can be reduced, and thus the temperature ofthe upper space above the separating plate can be reduced. Therefore,the temperature difference between the upper part and the lower part inthe upper space is also reduced, and the generation of convection of theinert gas due to the temperature difference can also be suppressed. As aresult, the influence on fluctuation in gas flow near the lower part ofthe preform influenced by the convection of the inert gas in the upperspace can be suppressed, and thereby fluctuation in heat transfer amountby the inert gas, and fluctuation in viscosity and softened amount ofthe glass are suppressed, so as to reduce fluctuation in diameter of theoptical fiber. Furthermore, because the influence by the convection ofthe inert gas in the upper space is reduced, the inert gas atmospherecan be maintained and the fluctuation in fiber diameter can besuppressed by flowing only a small amount of the inert gas near thepreform. Therefore, the amount of consumption of high cost inert gas,such as helium, is reduced, and thus an economical effect is alsoexpected.

Furthermore, by arranging an auxiliary heater outside the vicinity ofthe upper end of the inner tube to heat the vicinity of the upper partof the inner tube, the temperature inside the upper space can be furtheruniform.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a vertical cross sectional view showing a main part of anembodiment of the furnace for drawing an optical fiber according to theinvention;

FIG. 2 is vertical cross sectional views showing a main part of anotherembodiment of the furnace for drawing an optical fiber according to theinvention, where (A) is a figure showing the state at the beginning offiber drawing, and (B) is a figure showing the state near the completionof the fiber drawing;

FIG. 3 is an explanatory view of an example where a separating plate isprovided between a connecting part and a preform;

FIG. 4 shows another embodiment of the separating plates according tothe invention, where (A) is a perspective view thereof, and (B) is avertical cross sectional view showing the same near the part where theseparating plates are attached;

FIG. 5(A) is a vertical cross sectional view showing another embodimentof the separating plates according to the invention, and FIG. 5(B) is adetailed cross sectional view of one set of separating plates;

FIG. 6 is a perspective view showing another embodiment of theseparating plate according to the invention;

FIG. 7 is a vertical cross sectional view showing another embodiment ofthe furnace for drawing an optical fiber according to the invention,where (A) is a figure showing the state at the beginning of fiberdrawing, and (B) is a figure showing the state near the completion ofthe fiber drawing;

FIG. 8 is a vertical cross sectional view showing a main part of afurnace for drawing an optical fiber according to a prior art;

FIG. 9 is a vertical cross sectional view showing a main part of afurnace for drawing an optical fiber according to another prior art; and

FIG. 10 is a vertical cross sectional view showing a main part of afurnace for drawing an optical fiber according to another prior art;

BEST MODE FOR CARRYING OUT THE INVENTION

Embodiments of the furnace and the method for drawing an optical fiberaccording to the invention will be described with reference to FIGS. 1to 7.

FIG. 1 and 2 are vertical cross sectional views showing main parts ofembodiments of the furnace for drawing an optical fiber of theinvention. FIG. 1 shows an embodiment using plural separating plates,and FIG. 2 shows an embodiment using one set of separating plates. FIG.2(A) shows the state at the beginning of fiber drawing where the preformis large, and FIG. 2(B) shows the state before the completion of fiberdrawing where the preform has become small. In FIGS. 1 and 2, numeral 1denotes a preform, 1 a denotes an optical fiber, 2 denotes a dummy rod,3 denotes a connecting part, 4 denotes a separating plate, 5 and 5′denote an inner tube, 6 denotes an outer tube, 7 denotes a gas supplyinginlet, 7 a denotes a gas passage, 8 denotes a gas blowing inlet, 9denotes an upper lid, 10 denotes a muffle tube, 11 denotes a heater, and12 denotes a casing for downward extension of a furnace body.

In the case of FIGS. 1 and 2, the inner tube 5 or 5′ is arranged toconnect to an upper end of the muffle tube 10. Most of the muffle tube10 and the inner tube 5 generally have a cylindrical shape. In the caseof FIG. 1, the inner tube 5′ has a truncated cone shape where the innerdiameter thereof is gradually decreased from the upper part to the lowerpart. The preform 1 supported by the dummy rod 2 is arranged inside themuffle tube 10 and the inner tube 5 and 5′, and the vicinity of thelower end of the preform 1 is heated and melted by the heater 11 fromthe outside of the muffle tube 10, so as to draw the optical fiber 1 afrom the lower end of the preform 1.

The outer tube 6 is provided outside the inner tube 5 and 5′, and aninert gas is carried into the inside of the inner tube 5 and 5′ and themuffle tube 10 from the gas blowing inlet 8 provided on the wall of theinner tube 5 and 5′ through the gas supplying inlet 7 provided in theouter tube 6 to the gas passage 7 a. The upper end of the inner tube 5and 5′ is covered with an upper lid having a hole, through which thedummy rod 2 penetrates, to prevent the inert gas from exhausting.

A large number of positions, i.e., 10 or more, of the gas blowing inlets8 provided in the inner tube 5 and 5′ are provided on the wall near thelower end of the inner tube 5 and 5′ with substantially constantintervals, and the flow of the inert gas blown therefrom in the innertube 5 and 5′ is made as uniform as possible circumferentially. Aboutfour gas supplying inlets 7 are provided in the outer tube 6circumferentially.

Each set of separating plates 4 is in a plate form having a thickness offrom several millimeters to about 10 mm comprising a heat resistantmaterial, such as quartz, carbon, silicon carbide and the like, and inthe case where the inner tube has a cylindrical shape, it is of a diskshape, and in the case where the inner tube has a prismatic tube shape,it is of a polygonal shape corresponding to the shape of the inner wallthereof. The center hole diameter of each set of the separating platesis made larger than the outer diameter of the dummy rod 2 so as toabsorb the deviation from the concentric condition of the inner tube andthe dummy rod, and the center hole diameter is made smaller than thesize of the connecting part 3 of the dummy rod 2 and the preform 1, soas to place the separating plate 4 on the connecting part 3.

In the case of FIG. 1, the outer diameters of the respective plural setsof separating plates 4 are gradually decreased one by one from the upperones to the lower part corresponding to the inner diameters of the innertube 5′ having a truncated cone shape at the positions descending atsubstantially regular intervals from the upper end of the inner tube 5′.When the preform 1 becomes small with proceeding the drawing, theconnecting part 3 descends with the dummy rod 2, but the pluralseparating plates are stopped at substantially regular intervals on theinner wall surface of the inner tube one set by one set from theseparating plate at the upper part, because the plural separating plates4 are prevented from descending at the position where the inner diameterof the inner tube 5′ coincides with the outer diameter of the separatingplate 4.

In the example of FIG. 1, the plural sets of separating plates arestopped at intervals on the inner wall surface of the inner tube byusing a truncated cone shape inner tube 5′ and using the plural sets ofseparating plates having outer diameters gradually decreasing from theupper part to the lower part, but it is possible to employ anothermethod as a stopping method of the plural sets of separating plates. Forexample, by using disks having an outer diameter smaller than the innerdiameter of the inner tube as the plural sets of separating plates,about 2 to 4 protrusions are provided on the outer circumference of therespective disks circumferentially at regular intervals, and the outerdiameter connecting tips of the protrusions is made smaller than theinner diameter of the inner tube by 5 to 10 mm. The plural sets ofseparating plates are stacked on each other in such a manner that theprotrusions do not overlap. On the other hand, protrusion receivingparts are fixed on the inner wall of the inner tube at regular intervalsin the axial direction and circumferentially of the inner tube. Thecircumferential intervals of the protrusion receiving parts coincidewith the intervals of the protrusions of the separating plate. Thecircumferential positions of the protrusion receiving parts are shiftedby respective steps in the axial direction of the inner tube. Byconstituting the inner tube and the separating plates in the mannerdescribed above, the separating plates that are placed on a supportingmember of the dummy rod in a stacked form in the initial stage descendwith the dummy rod and are prevented from descending one set by one setfrom the upper part by stopping the protrusions on the outer peripheryof the separating plate with the protrusion receiving parts on the innerwall surface of the inner tube, and thus the space inside the inner tubecan be separated at regular intervals. In this method, however, there isa problem of positional alignment of the protrusions of the separatingplate and the protrusion receiving parts of the inner wall surface ofthe inner tube, and the like, and thus the method of FIG. 1 can beeasily handled in view of apparatus.

FIG. 2 shows an embodiment using one set of separating plates. In thiscase, the separating plate 4 is one plate having a disk form, and placedon the connecting part 3 of the dummy rod 2. The outer diameter of theseparating plate 4 is smaller than the inner diameter of the inner tube5 by about from 5 to 10 mm. It is also possible that the separatingplate 4 is not placed on the connecting part 3, but a supporting memberis fixed to the dummy rod 2, and the separating plate 4 is placedthereon, or it is directly fixed to the dummy rod 2. Furthermore, byproviding gap between the separating plate 4 and the dummy rod 2, theseparating plate 4 is prevented from damaging the inner tube 5 even whenthe dummy rod 2 and the preform 1 roll inside the inner tube 5. Sinceone set of separating plates has a function of separating the spaceabove the preform in the inner tube, an effect of stabilizing the streamof the inert gas inside the inner tube is obtained. It is morepreferable to use plural sets of separating plates to reduce turbulenceof the stream of the inert gas inside the space of the inner tube, fromthe standpoint of reducing the influence on fluctuation in diameter ofthe optical fiber on drawing, because the length of the inner tubebecomes 2 m or more.

A large space occasionally forms between the connecting part and thepreform depending on the shape of the preform. In this case, as shown inFIG. 3, the separating plates 4 are arranged at regular intervalsbetween the preform 1 and the connecting part 3, and in the tapered partat an upper part of the preform 1, and thus the space above the preforminside the inner tube can be separated into small parts to furtherincrease the separating effect.

Further embodiments of the separating plate 4 include those shown inFIGS. 4 and 5. FIG. 4(A) is a perspective view of one set of separatingplates, and FIG. 4(B) is a vertical cross sectional view showing thestate where one set of separating plates is arranged inside the innertube. FIG. 5(A) is a vertical cross sectional view showing the statewhere plural sets of separating plates are arranged, and FIG. 5(B) is adetailed cross sectional view of one set of separating plates. In theseexamples, the set of separating plates 13 or 14 is constituted by aninner member 13 a or 14 a and an outer member 13 b or 14 b. Thematerials are the same as the cases of FIGS. 1 and 2. The outer diameterof the outer member 13 b and 14 b is smaller than the inner diameter ofthe inner tube 5 or is the same as the inner diameter of the inner tube5′ at the position where the outer member is stopped, and the centerhole diameter of the outer member 13 b and 14 b is larger than the outerdiameter of the dummy rod 2 so as to absorb the deviation from theconcentric condition of the inner tube and the dummy rod. The outerdiameter of the inner member 13 a and 14 a is larger than the centerhole diameter of the outer member 13 b and 14 b and is smaller than theouter diameter of the outer member 13 b and 14 b. The center holediameter of the inner member 13 a and 14 a is slightly larger than theouter diameter of the dummy rod 2. In the example of FIG. 4(B), theinner member 13 a of one set of separating plates 13 is placed on theconnecting part 3, and the outer member 13 b is placed on the innermember 13 a. Consequently, even when the dummy rod 2 rolls to the rightand left inside the inner tube 5 to break the concentric condition, theseparating plate 13 can be prevented from damaging the inner tube 5,because the outer member 13 b follows by sliding on the inner member 13a.

While FIG. 4 shows an example where both the outer member and the innermember are of a disk shape, in the case where the inner tube has aprismatic tuber shape, at least the outer peripheral shape of the outermember necessarily has a polygonal shape. With respect to the outerdiameter and the inner diameter, they can be considered as distances tothe outer circumference and the inner circumference measured from thecenter in the same direction.

The example of FIG. 5(A) shows an embodiment where the respective setsof separating plates 14 except for the lowermost separating plate 15 areeach constituted by an outer member 14 b and an inner member 14 a. Inthis example, the inner tube 5′ is of a truncated cone shape, and theouter diameters of the separating plates 14, i.e., the outer diametersof the outer members 14 b, are decreased from the upper part to thelower part and coincide with the inner diameters of the inner tube atthe parts where the plates are stopped. In the example of FIG. 5(A), inthe respective sets of separating plates 14 the outer member is placedat the lower side and the inner member is placed at the upper side.

As described in the foregoing, when the plural sets of separating plates14 penetrated by the dummy rod 2 are placed on the connecting part 3,during descending the dummy rod 2 and so on while proceeding with thefiber drawing, the outer members 14 b are stopped on the inner wallsurface of the inner tube 5′ in the order from the uppermost separatingplate 14, with the inner members 14 a being prevented from movingdownward in the state where they are placed on the outer member 14 b ofthe respective sets, and thus the space inside the inner tube 5 isvertically separated by the respective sets of separating plates 14.While an example is shown in FIG. 5(A), where the plural sets ofseparating plates are respectively constituted by an outer member and aninner member except for the lowermost one, it is possible that only apart of the sets or all the plural sets of separating plates includingthe lowermost one are constituted by the outer members and the innermembers. Not using the combination of the outer member and the innermember, the space may be separated by one separating plate. As shown inFIG. 5(B), when a taper where the diameter is reduced toward the upside,is provided on the outer circumference 14 c of the outer member 14 b,the contact area with the inner tube 5′ can be reduced, and thepossibility of damage to the inner tube 5′ by the separating plate 14can be reduced.

As shown in FIG. 6, when protrusions 16 a having a hemispherical shapetoward the outside are provided at regular intervals on the outercircumference of the separating plate 16, the sliding frictioncoefficient of sliding on the inner wall surface of the inner tube canbe reduced during descending the separating plate in the inner tube.Such protrusions can be provided on the outer circumference of the outermember not only for the case of one separating plate, but also for thecases of a combination of two plates as in FIGS. 4(A) and (B) and FIG.5, so as to obtain a similar effect.

FIG. 7 shows cross sectional views showing an embodiment in which theseparating plate comprises a heat insulating material, where (A) showsthe state in the beginning of fiber drawing, and (B) shows the statenear the completion of the fiber drawing. The same symbols as in FIG. 1show the same components. Numeral 17 denotes a separating plate, 18denotes an auxiliary heater, 19 a denotes an upper space, and 19 bdenotes a lower space. The separating plate 17 comprising a heatinsulating material can make the temperature near the lower end of thedummy rod at 400° C. or less owing to the heat insulating effectthereof. A heat insulating material formed of carbon felt can be used.The thickness of the heat insulating material is about 30 to 150 mm.There are cases where the upside and downside thereof are retained withquartz plates having a thickness of about 10 mm. By providing theseparating plate comprising the heat insulating material, thetemperature above the separating plate can be lowered to about 300 to400° C. even when the temperature near the upper end of the preform isabout 1,200° C. By increasing the thickness of the heat insulatingmaterial, the temperature above the separating plate can be furtherlowered. A separating plate comprising materials such as one obtained bycompressing carbon powder, foamed ceramics, foamed quartz and the like,can be used provided that the heat insulating function equivalent to theheat insulating material can be realized.

Because the temperature of the lower part inside the upper space 19 acan be lowered by fabricating the separating plate 17 with a heatinsulating material, the convection of the inert gas retained in theupper space 19 a, due to the temperature difference inside the upperspace 19 a, scarcely occurs. Therefore, it scarcely occurs that theconvection of the inert gas in the upper space 19 a influences the gasstream in the vicinity of the fiber drawing part of the preform.

When the auxiliary heater 18 is provided outside the upper end of theinner tube 6 to heat the vicinity of the upper end of the inner tube 6to about 400° C., the vertical temperature difference inside the upperspace 19 a is further reduced, so as to further proceed with thetemperature uniformity. Thus, the gas convection inside the upper spacecan be further suppressed by the temperature uniformity in the upperspace 19 a. In this case, since the temperature inside the upper space19 a is lowered by the separating plate, it is not necessary to providea number of auxiliary heaters vertically. Only one auxiliary heateroutside the upper part of the inner tube may sufficiently exhibit theeffect.

In the furnace for drawing an optical fiber of this invention, becausethe separating plates 4 or 17 is provided around the dummy rod 2 orbetween the dummy rod 2 and the preform 1, and the gas blowing inlets 8are provided on the wall of the inner tube under the moving range of theseparating plate 4 and 17, the space between the separating plate 4 and17 and the preform 1 is always constant even when the preform isshortened with proceeding the drawing from the preform, so that there islittle upward stream from the gas blowing inlets 8, and thus it isconsidered that turbulence of the gas stream between the preform and theseparating plate does not occur. While the inert gas partially entersinto the upper space separated by the separating plate 4 and 17, thestream of the inert gas in the space does not influence the lower spaceunder the separating plate 4 and 17 because the stream is small.

Therefore, the inert gas entering from the gas blowing inlets 8 scarcelyflows toward the upper part of the preform, but flows downward to thecasing 12 for downward extending a furnace body, and therefore thestream of the inert gas around the drawn optical fiber 1 a is maintainedto laminar flow conditions. Since the stream is substantially unchangedby the descent of the preform, the fluctuation in diameter of theoptical fiber drawn from the lower end of the preform can be made small.

Optical fibers having a diameter of 125 μm were drawn from a preformhaving a diameter of 90 mm and a length of 1,500 mm in furnaces fordrawing an optical fiber shown in FIG. 1, FIG. 2 and FIG. 7, andfluctuation in diameter of the optical fibers could be suppressed to±:0.1 μm or less in each case.

Industrial Applicability

The furnace and a method for drawing an optical fiber of the inventioncan be utilized for the operation of producing an optical fiber bydrawing from a preform comprising glass, such as silica glass, as a maincomponent.

What is claimed is:
 1. A furnace for drawing an optical fiber comprisinga muffle tube and an inner tube connected to an end of the muffle tube,arranging inside said muffle tube and said inner tube a preformsupported by a dummy rod at an upper part thereof, in such a manner thatsaid preform descends with said dummy rod and said preform is melted bya heater arranged outside of said muffle tube, so as to draw an opticalfiber from the lower end of said preform, wherein one or morepartitions, each partition, comprising one or two separating plates,separate a space inside said inner tube above said preform into pluralpart in an advancing direction of said preform arranged inside saidspace, and descending with said preform during drawing an optical fiber,and a gas blowing inlet for blowing an inert gas into said inner tubeand said muffle tube is provided at the wall of said inner tube at apart under said separating plate, wherein said one or more partitionsare two or more partitions and the separating plates being penetrated bysaid dummy rod descend with said dummy rod, and the respective two ormore partitions of separating plates are stopped one by one on saidinner wall of said inner tube from an upper part, the outer diameters ofsaid respective separating plates of the two or more partitions decreasegradually one by one from the upper part to the lower part, said innertube has a truncated cone shape by decreasing the inner diameter thereoffrom the upper part to the lower part, said plural partitions ofseparating plates descend with said dummy rod, and said pluralpartitions of separating plates are stopped in their descent onepartition by one partition from the upper part owing to the contact ofthe outer periphery of said separating plate with the inner wall of saidinner tube.
 2. A furnace for drawing an optical fiber comprising amuffle tube and an inner tube connected to an end of the muffle tube,arranging inside said muffle tube, and said inner tube a preformsupported by a dummy rod at an upper part thereof, in such a manner thatsaid preform descends with said dummy rod and said preform is melted bya heater arranged outside of said muffle tube, so as to draw an opticalfiber from the lower end of said preform, wherein one or morepartitions, each partition comprising one or two separating plates,separate a space inside said inner tube above said preform into pluralparts in an advancing direction of said preform arranged inside saidspace, and descending with said preform during drawing an optical fiber,and a gas blowing inlet for blowing an inert gas into said inner tubeand said muffle tube is provided at the wall of said inner tube at apart under said separating plate, characterized in that said onepartition or plural partitions, each partition comprising one or twoseparating plates, arranged in the vicinity of the lower end of saiddummy rod or the upper part of said preform to descend with saidpreform, wherein at least one of said one partition or plural partitionsis composed of an outer member and an inner member, the outer diameterof said outer member is smaller than the inner diameter of said innertube, the center hole diameter of said outer member is larger than theouter diameter of said dummy rod so as to absorb the deviation from aconcentric condition of said inner tube and said dummy rod, the outerdiameter of said inner member is larger than said center hole diameterof said outer member and smaller than said outer diameter of said outermember, the center hole diameter of said inner member is the same as orlarger than said outer diameter of said dummy rod, and said dummy rodpenetrates through said center hole while said inner member is fixed tosaid dummy rod or is placed on a supporting member fixed to said dummyrod, and said outer member is placed on said inner member.
 3. A furnacefor drawing an optical fiber comprising a muffle tube and an inner tubeconnected to an end of the muffle tube, arranging inside said muffletube and said inner tube a preform supported by a dummy rod at an upperpart thereof, in such a manner that said preform descends with saiddummy rod and said preform is melted by a heater arranged outside ofsaid muffle tube, so as to draw an optical fiber from the lower end ofsaid preform, wherein one or more partitions, each partition comprisingone or two separating plates, separate a space inside said inner tubeabove said preform into plural parts in an advancing direction of saidpreform arranged inside said space, and descending with said preformduring drawing an optical fiber, and a gas blowing inlet for blowing aninert gas into said inner tube and said muffle tube is provided at thewall of said inner tube at a part under said separating plate, whereineach separating plate has plural protrusions provided on the outerperiphery of the separating plate, so as to prevent parts of saidseparating plate other than said protrusions from contacting said innerwall surface of said inner tube.
 4. A furnace for drawing an opticalfiber comprising a muffle tube and an inner tube connected to an end ofthe muffle tube, arranging inside said muffle tube and said inner tube apreform supported by a dummy rod at an upper part thereof, in such amanner that said preform descends with said dummy rod and said preformis melted by a heater arranged outside of said muffle tube, so as todraw an optical fiber from the lower end of said preform, wherein one ormore partitions, each partition comprising one or two separating plates,separate a space inside said inner tube above said preform into pluralparts in an advancing direction of said preform arranged inside saidspace, and descending with said preform during drawing an optical fiber,and a gas blowing inlet for blowing an inert gas into said inner tubeand said muffle tube is provided at the wall of said inner tube at apart under said separating plate, wherein each said separating platecomprises a heat insulating material formed of carbon felt.